Tiah Curing & Sealing Compound | Bierschbach

Manufacturer W.R.Meadows

Model Number TIAH


TIAH acrylic concrete curing and sealing compound is an acrylic polymer solution that dries to a transparent film, which improves abrasion resistance of the concrete.
TIAH provides a tough, clear film that will not after-yellow. It also provides improved weather and stain resistance, combined with a dustproof sealer.


TIAH is used on driveways, patios, industrial floors, loading docks, swimming pool areas, and exposed aggregate, as well as any exterior surface where protection and sealing of concrete is desired (dries to a low medium sheen). TIAH offers improved resistance to rain, sun, freezing temperatures, stains, most acids and industrial chemicals, oil, grease, de-icing salts, cleaning agents (except aromatic solvents), and caustics, as well as airborne soot, dust, and other pollutants.


Applies easily u0085 dries to the touch in 30 u0096 60 minutes.
Permeable film allows moisture in cured concrete to evaporate
Provides a clear, tough, easy-to-clean film, which improves abrasion and stain resistance.
Offers improved resistance to rain, sun, freezing temperatures, most acids and industrial chemicals, oil, grease, de-icing salts, cleaning agents (except aromatic solvents), caustics, airborne soot, dust, and other pollutants.
Offers excellent foot or vehicular traffic wearing qualities.
Recoat after thorough surface cleaning to restore original beauty.
Concrete sealed with TIAH can later be painted (consult reputable paint manufacturer for compatibility) or covered with resilient flooring or carpeting, if desired.
Dried film is USDA accepted.
VOC compliant u0085 meets U.S. EPA Architectural Coatings Rule requirements

1 Gallon (3.79 Liter) Cans (6 per carton)
5 Gallon (18.93 Liter) Pails
55 Gallon (208.20 Liter) Drums

300 u0096 600 ft.u00b2/gal. (7.37 -14.73 mu00b2/L), depending on surface finish. Coverage may vary due to porosity and condition of the concrete

AASHTO M 148, Type 1, Classes A B
ASTM C 309, Type 1, Classes A B
ASTM C 1315, Type I, Class A
Dried film is USDA accepted
Complies with U.S. EPA maximum allowable VOC requirements

Surface Preparation u0085 Existing Concrete: Concrete surfaces must be clean and dry with all stains, oil, grease, dust, and dirt removed prior to application. We recommend ULTRITEu00ae DEGREASERfrom W. R. MEADOWS for cleaning. New Concrete: TIAH should be applied when surface water has completely disappeared and the concrete surface will not be marred by walking workmen.Application Method u0085 Use a sprayer or short-nap roller to apply a uniform film. Avoid puddling in low areas. If puddles occur, brush or roll them out. A standard industrial-grade sprayer, equipped with a neoprene hose and gaskets, as well as a 5941 spray nozzle (or equivalent) is recommended for best results.
For optimum performance, apply first coat at 600 ft.u00b2/gal. After the first coat has thoroughly dried, apply a second coat at 600 ft.u00b2/gal. NOTE: Second coat should be applied at a right angle.
Drying Time u0085 TIAH dries quickly. Drying times may be extended depending on application rate, temperature, humidity, and project conditions. Restrict foot traffic for at least four hours. Twelve hours is preferable.
Cleanup u0085 Application equipment should be cleaned promptly after use with xylene or toluene.

DO NOT DILUTE. FOR EXTERIOR APPLICATION ONLY. Surfaces treated with TIAH may become slippery under certain conditions.TIAH should not be applied during high temperature conditions in direct sunlight. These conditions cause rapid evaporation, which does not allow the film to form properly. Under these conditions, the film may peel, bubble, and/or turn white (blush). TIAH should not be applied to concrete exposed to excessive moisture. Entrapped moisture in a solvent-based sealer may cause the film to peel and/or turn white (blush).

Do not apply TIAH if the temperature of the concrete is below 40u00ba F (4u00ba C). TIAH may be used on colored concrete, but mottling may occur. Do not use on dense or non-porous surfaces, i.e. brick, stone, etc. Do not use TIAH as a waterproofing sealer on masonry surfaces. TIAH is a membrane-forming sealer. All membrane-forming sealers may darken the concrete or magnify imperfections caused by variations in the porosity of the concrete.

Concrete containing calcium chloride will remain dark longer when treated with TIAH. A small test patch application is recommended. Concrete floors properly cured with TIAH meet section 8.9 u0093Adhesion of Tile Cementsu0094 of ASTM C 1315. For other specifications, secure the approval of the paint or resilient flooring manufacturer before applying TIAH. The specifier and user shall determine the suitability of product for specific applications and assume all responsibility in connection therewith.

Refer to Material Safety Data Sheet for complete health and safety information.