LIQUI-HARD concrete densifier and chemical hardener compound is a proprietary, water-based, ready-to-use, clear silicate liquid, formulated with chemically reactive raw materials to harden and dustproof concrete. This waterborne solution, when properly applied, offers substantial improvement in abrasion and chemical resistance and will significantly improve the durability of the concrete surface when compared to untreated concrete. As LIQUI-HARD is applied and penetrates into the concrete surface, a chemical reaction takes place, producing a byproduct that fills in the pores of the concrete. This process produces a substantially denser concrete surface with enhanced durability. In addition to the densifying and hardening action, LIQUI-HARD also solidifies the concrete, eliminating dusting and pitting.
USES LIQUI-HARD is recommended for use wherever hardened, dustproofed, and improved chemical- and abrasion-resistant surfaces are required. Ideal applications include floors in industrial plants and warehouses, storage silos, sewage plants, chemical processing facilities, refineries, and heavy pedestrian floor traffic areas, such as civic centers, sports arenas, stadiums, hospitals, airports, and museums. LIQUI-HARD can successfully be used in conjunction with shake-on hardeners.
FEATURES/BENEFITS Penetrates deeply into concrete to densify and harden surfaces to help prevent entry of moisture and other foreign matter.
Dustproofs and improves chemical, petroleum, and abrasion resistance of treated surfaces.
Provides a permanent, attractive sheen with the ability to polish.
Protects against scratching or peeling.
Provides tough, protected surface that wonu0092t after-yellow, discolor, or show pedestrian or vehicular traffic wear marks.
SHELF LIFE When stored indoors in original, unopened containers at temperatures between 40u00b0 u0096 90u00b0 F (4u00b0 u0096 32u00b0 C), optimum performance and best use is obtained within one year of date of manufacture.
SPECIFICATIONS Complies with U.S. EPA, LADCO, OTC, SCAQMD, and all other current North American VOC regulations. Treated surface is USDA accepted.
TECHNICAL DATA VOC Content: 0 g/L
Surface Preparation u0085 Fresh Concrete: On newly placed concrete, LIQUI-HARD can be applied after final troweling. Existing (Old) Concrete: Surface should be clean and structurally sound. Remove all residues, curing compounds, oils, sealers, contaminants, and laitance before applying LIQUI-HARD. ULTRITEu00ae DEGREASER from W. R. MEADOWS may be used for cleaning. Fill and repair all holes, cracks, and deteriorated areas that have been removed to sound concrete.
For optimum results on fresh, newly placed concrete, use MED-CUREu0099 curing aid from W. R. MEADOWS immediately after final finishing operations have been completed. Apply LIQUI-HARD according to the below existing concrete directions a minimum of three days after placement of concrete.
Mixing u0085 For optimum performance, gentle mixing or agitation is recommended.
Application Method u0085 Fresh Concrete: Apply undiluted LIQUI-HARD at approximately 300 ft.2/gal. (4.91 m2/L) using a low-pressure sprayer, such as a Chapin 1949 with a 0.5 GPM (1.9 LPM) spray nozzle, or by spreading evenly with a soft-bristled broom. Do not allow material to puddle on the surface. No further application steps are required for fresh concrete. Existing (Old) Concrete: Saturate the surface with undiluted LIQUI-HARD by sprayer, squeegee or broom. Keep the surface wet with LIQUI-HARD for a minimum of 30 minutes. (A range of 30 u0096 60 minutes may be required depending on temperature and conditions.) NOTE: Pay particular attention to porous and/or dry areas. These areas must be kept wet at all times with LIQUI-HARD. Once the surface begins to gel and becomes slippery, immediately spray the surface with a light water mist. Scrub the surface with a broom or mechanical scrubber to increase the penetration of the LIQUI-HARD. Continue to work the LIQUI-HARD into the surface for another 5 u0096 10 minutes or until LIQUI-HARD becomes gelled and slippery for a second time. At this time, THOROUGHLY flush the surface with water. During the flushing process, agitate the surface with a broom to aid in removal of the excess LIQUI-HARD. Remove all excess material with a mop or squeegee. Thoroughly squeegee the surface dry. If there are slippery patches, this is an indication that there is still excess LIQUI-HARD present. These areas should be re-flushed and squeegeed again until the entire surface is dry. (Extremely porous surfaces may require a second application.) WARNING: Failure to thoroughly wash and remove all excess material from floor surfaces may result in unsightly white stains. Immediately wash off over-spray from glass, aluminum, or highly polished surfaces with water to avoid etching of surfaces. For application assistance, contact W. R. MEADOWS at (800) 342-5976.
Burnishing u0085 LIQUI-HARD can be burnished to a high sheen on steel trowel concrete floors. A high-speed burnisher (2000 u0096 2200 rpm) with appropriate maintenance pad is needed.
Drying Time u0085 2 u0096 4 hours. LIQUI-HARD dries very quickly on new, virgin concrete. Drying times may be extended on existing (old) concrete due to surface conditions. Restrict foot traffic for at least four hours; 12 hours is preferable.
Cleanup u0085 While still wet, equipment may be cleaned quickly and easily with soap and water. Do not allow LIQUI-HARD to dry before flushing excess from surfaces.
PRECAUTIONS DO NOT DILUTE. Do not apply if the temperature of the concrete is less than 35? F (2? C) or above 135? F (57? C). KEEP FROM FREEZING. If frozen, product should be thawed and agitated slightly prior to use.
HEALTH HAZARDS LIQUI-HARD is non-combustible. (Flash point is greater than 210? F.) Direct contact will result in irritation of the skin and eyes. Inhalation of product mist may result in respiratory irritation. Refer to Safety Data Sheet for complete health and safety information.
LEED INFORMATION May help contribute to LEED credits: IEQ Credit 4.2: Low-Emitting Materials: Paints and Coatings IEQ Credit 4.3: Low-Emitting Materials u0096 Flooring Systems MR Credit 2: Construction Waste Management MR Credit 5: Regional Materials